Attributs du produit

Modèle: ASTM A335 P5

marque: H-tong

La Norme: bs, GB, ASTM, JIS, VACARME, API

Matériel: 10MoWVNb, MO, 10Cr9Mo1VNb, Alliage Mn-V, Alliage Cr-Mo, 15NiCuMoNb5, 10 # -45 #, Alliage CrNi, Q195-Q345

Forme De La Section: Rond

Lieu D'origine: Chine

Application: Tuyau de fluide, Tuyau de chaudière, Tuyau de forage, TUYAU D'HUILE, Tuyau de structure, Tuyau hydraulique, Tuyau de gaz

Certification: Bsi, ce, API

Tube Spécial: Pipe API, Tuyau à paroi épaisse

Que Ce Soit En Alliage: Est un alliage

Tolérance: ± 1%

Catégorie: Tuyau en acier sans soudure

Service De Traitement: Pliant, Soudage, Décollage, Perforation, Coupe

Section Shape: Round

Technique: Cold Rolled

Origin: China

HS Code: W005

Outer Diameter: 3 - 80 mm or According to Customer Requirements

Thickness: 0.5-8mm or According to Customer Requirements

Surface: Black Painted,PE Coated,Galvanized,Varnished,HDPE,etc

Surface Treatment: As Per Customer's Request

Grade: 10#, 20#, 45#, 16mn, A213, 35CRMO4, 30CrMo, Q235

Application: Fluid Pipe or Boiler Pipe

Processus De Production: Laminé à chaud

Emballage & livraison

Unités de vente	:	Ton
Type de colis	:	Papier anti-eau et plastique ou recouvert de feuille de fer ou attaché à trois bandes de cerclage
Exemple d’image	:
Télécharger	:

Tuyau en acier en alliage

Tuyau en acier allié



Description du produit

Présentation du produit

ASTM A335 S EAMOLUX A LLOY S TEEL P IPE

Le tuyau ASTM A335 (ASME S / A335, Chorme-Moly) est un tuyau en acier en alliage ferritique transparent pour un service à haute température. Le tuyau commandé à cette spécification doit être adapté à la flexion, aux flancs (vanstoning) et aux opérations de formation similaires, et pour le soudage de fusion. Parfois appelé «grade de p», le tuyau chromé de moly est populaire dans les grades P p5, p9, p11, p22 et p91. L'utilisation la plus courante des classes P11, P22 et P91 se trouve dans l'industrie de l'énergie et les plantes pétro-chimiques, les grades P5 et P9 sont couramment utilisés dans les raffineries.

L'A335 est souvent appelé tuyau chromé moly en raison de la composition chimique du molybdène (MO) et du chrome (CR). Le molybdène augmente la résistance de l'acier ainsi que la limite élastique, la résistance à l'usure, les qualités d'impact et la durabilité. Moly augmente la résistance à l'adoucissement, restreint la croissance des grains et rend l'acier au chrome moins sensible à la fragilisation. Moly est l'additif unique le plus efficace qui augmente la résistance au fluage à haute température. Il améliore également la résistance à la corrosion de l'acier et inhibe les piqûres. Le chrome (ou chrome) est le constituant essentiel de l'acier inoxydable. Tout acier avec 12% ou plus de chrome est considéré comme un acier inoxydable. Le chrome est pratiquement irremplaçable pour résister à l'oxydation à des températures élevées. Chrome augmente la traction, le rendement et la dureté à des températures ambiantes. La composition du tuyau en acier en alliage en alliage Moly le rend idéal pour une utilisation dans les centrales électriques, les raffineries, les usines de produits chimiques de Petro et les services de champ d'huile où les liquides et les gaz sont transportés à des températures et des pressions extrêmement élevées.

S TOCKS Une gamme complète des classes de tuyaux A335 suivantes:

Spécification standard pour la chaudière en alliage ferritique et austénitique sans couture, les tubes en alliage en alliage, surchauffeur et les tubes d'échangeurs de chaleur .

Cette spécification couvre la chaudière en acier ferritique et austénitique sans couture et les tubes à échanges de chaleur. Les notes contenant la lettre H de leur désignation ont des exigences différentes de celles des grades similaires ne contenant pas la lettre H. Ces différentes exigences fournissent une force de rupture de fluage plus élevée que normalement réalisable dans des grades similaires sans ces exigences différentes. Les tubes doivent être fabriqués par le processus sans couture et doivent être finis à chaud ou à froid, comme spécifié. Grade TP347HFG doit être terminé à froid. Le traitement thermique doit être effectué séparément et en plus du chauffage pour la formation à chaud. L'alliage ferritique et les aciers inoxydables ferritiques doivent être réchauffés. D'un autre côté, les tubes en acier inoxydable austénitique doivent être fournis à l'état thermique. Alternativement, immédiatement après la formation à chaud, tandis que la température des tubes n'est pas inférieure à la température minimale de la solution, les tubes peuvent être éteintes individuellement dans l'eau ou rapidement refroidis par d'autres moyens. Le test de tension, le test de dureté, le test d'aplatissement et le test d'évasement doivent être effectués à chaque tube. De plus, chaque tube doit être soumis au test électrique non destructif ou à un test hydrostatique.

Spécification de produit

Item	Cold rolled/Hot rolled alloy steel seamless pipe
Standard	ASTM A209M/ASME 209M, ASME SA210, ASTM A213/ASME SA213M ASTM A333M/ASME SA333/SA333M, ASTM A334M/ASME SA334/SA334M ASTM A335/ASME SA335, ASTM A519, ASTM A691 GB3087, GB6479-2000, GB9948-2006, GB5310-2013, GB5310-95, GB9948-88 DIN 17175, EN10216-2, JISG3467, JISG3458, JIS G3441, NF A49-213/215, BS3059, BS3604, BS3606
Materials	A209 T1/SA209 T1, A209 T1b/SA-209 T1b, A209 T1a/SA209 T1a. T2, T5, T9, T11, T12, T22, T23, T24, T91, T911, T92, T122. P1, P2, P5, P5b, P5c, P9, P11, P12, P21, P22, P23, P24, P91, P92. 4118, 4130, 4135, 4137, 4140. 20G, 25MnG, 15MoG, 15CrMoG, 20MoG, 12CrMoG, 12Cr2MoG, 12Cr1MoVG, 12Cr2MoWVTiB, 10Cr9Mo1VNb, 15CrMoG, 10CrMo910. ST35.8, ST45.8, 15Mo3, 13CrMo44, 10CrMo910, 14MoV63,12Cr1MoV. P195GH, P235GH, P265GH, 13CrMo4-5, 10CrMo9-10, 16Mo3, 10CrMo5-5, X10CrMoVNb9-1. GRADE 91, CM65, CM70, CM75, CMSH70, CMS75, CMSH80. GRADE 1/2 Cr, GRADE 1CR, GRADE 1 1/4 CR, 2 1/4 Cr, 3CR, 5CR, 9CR. STPA12, STPA20, STPA22, STPA23, STPA24, STPA25, STPA26. SCR420 TK,SCM415 TK, SCM418 TK, SCM420TK, SCM430TK, SCM435TK, SCM440TK. TU15D3, TU13CD4-04, TU10CD910, TUZ10CD505. S1-622-440, S2-622-440, S1-622-490, S2-622-490, S1-629-470, S2-629-470, S2-629-590. HFS625 CFS625, CFS625.
Description	Surface	black painted, PE coated, galvanized
	Length	5.8m, 6m, 11.8m, 12m, or as required
	Wall Thickness	1-120mm
	Outer Diameter	6-1200mm
Trade terms	Payment terms	T/T, L/C, D/P
	Price terms	FOB, CIF
Package	Standard export seaworthy package or as required.
Delivery time	Prompt delivery or as the order quantity.
Export to	Alloy steel pipe applies to petroleum,chemical industry, electric power, boiler, high temperature resistant, low temperature resistant,corrosion resistant seamless steel pipe used.Alloy steel pipealso can made according to the customer.
Container size	20ft GP:5898mm(Length)x2352mm(Width)x2393mm(High) 24-26CBM 40ft GP:12032mm(Length)x2352mm(Width)x2393mm(High) 54CBM 40ft HC:12032mm(Length)x2352mm(Width)x2698mm(High) 68CBM
Contact	If you have any question,please feel free to contact me.

ASTM A3 3 5 Pipe d'acier en alliage sans couture

L'A335 est souvent appelé tuyau chromé moly en raison de la composition chimique du molybdène (MO) et du chrome (CR). Le molybdène augmente la résistance de l'acier ainsi que la limite élastique, la résistance à l'usure, les qualités d'impact et la durabilité. Moly augmente la résistance à l'adoucissement, restreint la croissance des grains et rend l'acier au chrome moins sensible à la fragilisation. Moly est l'additif unique le plus efficace qui augmente la résistance au fluage à haute température. Il améliore également la résistance à la corrosion de l'acier et inhibe les piqûres. Le chrome (ou chrome) est le constituant essentiel de l'acier inoxydable. Tout acier avec 12% ou plus de chrome est considéré comme un acier inoxydable. Le chrome est pratiquement irremplaçable pour résister à l'oxydation à des températures élevées. Chrome augmente la traction, le rendement et la dureté à des températures ambiantes. La composition du tuyau en acier en alliage en alliage Moly le rend idéal pour une utilisation dans les centrales électriques, les raffineries, les usines de produits chimiques de Petro et les services de champ d'huile où les liquides et les gaz sont transportés à des températures et des pressions extrêmement élevées.

Composition chimique:

Grade	ASTM A335 P5	ASTM A335 P9	ASTM A335 P11	ASTM A335 P12	ASTM A335 P22	ASTM A335 P91
Carbon	≤0.15	≤0.15	0.05 – 0.15	0.05 – 0.15	0.05 – 0.15	0.08 – 0.12
Manganese	0.30 – 0.60	0.30 – 0.60	0.30 – 0.60	0.30 – 0.60	0.30 – 0.60	0.30 – 0.60
Phosphorous	≤0.025	≤0.025	≤0.025	≤0.025	≤0.025	≤0.020
Sulfur	≤0.025	≤0.025	≤0.025	≤0.025	≤0.025	≤0.010
Silicon	≤0.50	0.25 – 1.00	0.50 – 1.00	≤0.50	≤0.50	0.20 -0.50
Chromium	4.00 – 6.00	8.00 – 10.00	1.00 – 1.50	0.80 – 1.25	1.90 – 2.60	8.00 – 9.50
Molybdenum	0.45 -0.65	0.90 – 1.10	0.44 – 0.65	0.44 – 0.65	0.87 – 1.13	0.85 – 1.05

Propriétés mécaniques:

Tensile Strength, min., psi	P-5	P-9	P-11	P-22	P-91
ksi	60	60	60	60	85
MPa	415	415	415	415	585
Yield Strength, min., psi
ksi	30	30	30	30	60
MPa	205	205	205	205	415

Tensile Strength, min., psi		P-5	P-9	P-11	P-22	P-91	P91 shall not have a hardness not exceeding 250 HB/265 HV [25HRC].
	ksi	60	60	60	60	85
	MPa	415	415	415	415	585
Yield Strength, min., psi
	ksi	30	30	30	30	60
	MPa	205	205	205	205	415

Affichage de produit

Nous pouvons produire différentes tailles, épaisseurs, largeurs et matériaux en fonction de vos exigences

alloy pipe

alloy pipe Alloy Steel pipe

Test de produit

Nous contrôlerons la qualité à partir d'une partie du tuyau d'acier de matériau, chaque tuyau produit sera qu'il est propre étiquette d'identification, la qualité vérifiera le composant chimique et la propriété physique, puis fournira un certificat de test de matériau. La dimension de taille sera vérifiée et afficher les images au client pour garantir que toutes les marchandises répondront aux exigences.

Acceptez l'inspection d'un tiers désigné / payé par l'acheteur, comme SGS, BV.

Reconnu par des clients en Malaisie, en Indonésie, à Singapour, aux Philippines, en Australie, au Pérou et au Royaume-Uni. Nous avons des certificats ISO9001 / 18001, CE.