Plaque en acier en carbone de résistance à usure roulée NM400 à chaud NM400
Obtenir le dernier prixType de paiement: | T/T,L/C,D/P |
Incoterm: | FOB,CFR,CIF,EXW |
transport: | Ocean,Land,Express |
Hafen: | Qingdao,Tianjin,Shanghai |
SHANDONG HUITONG STEEL CO.,LTD
Type d'Affaires:Société de commerce , Fabricant
principaux marchés: Afrique , Asie , Europe de l'Est , L'Europe , À l'échelle mondiale
Exportateur:51% - 60%
certs:ISO9001, API, ASME, CE
La description:Plaque d'acier de résistance à l'usure NM400,NM400 Portez une plaque d'acier,Plaque d'acier de résistance à l'usure
Type de paiement: | T/T,L/C,D/P |
Incoterm: | FOB,CFR,CIF,EXW |
transport: | Ocean,Land,Express |
Hafen: | Qingdao,Tianjin,Shanghai |
Modèle: NM400
marque: H-tong
Standard: Astm, Gb, Aisi, Din
Place Of Origin: China
Species: Steel Plate
Production Process: Hot Rolled
Application: Boiler Plate, Container Plate, Ship Plate
Special Steel: Wear Resistant Steel, High-Strength Steel Plate
Tolerance: ±1%, ±3%
Category: Hot Rolled Steel Sheet, Boiler Vessel Plate, Cold Rolled Steel Sheet, Steel Plate, Low-Alloy Plate, Ship Steel Plate
Processing Service: Cutting, Welding, Decoiling, Bending, Punching
Surface Treatment: Coated
Unités de vente | : | Ton |
Type de colis | : | paquet avec une bande d'acier |
Exemple d’image | : |
Plaque d'usure de superposition en carbure de chrome sont fabriqués en soudant une ou plusieurs couches résistantes à l'usure sur une plaque de base en acier moyen ou faible en carbone.
L'alliage de superposition a une grande quantité de particules dures en carbure de chrome qui font que la plaque a une bonne usure et une résistance à l'impact.
Plage d'épaisseur de superposition : 3-25 mm
Taille de la plaque d'usure: 1500 * 3000, 1400 * 3000,1400 * 3400, 1400 * 3500, 2100 * 3500, personnalisée.
La plaque d'acier d'usure de superposition en carbure de chromé est utilisée pour faire positionner de nombreuses pièces d'usure complexes dans des endroits à usage élevé.
Nous pouvons fournir une coupe, une flexion, un boulonnage, un coup de poing et un soudage en fonction des dessins du client.
La plaque d'acier résistante aux vêtements est composée d'une plaque en acier à faible teneur en carbone et d'une couche résistante à l'usure en alliage. Lorsque vous travaillez, la matrice fournit des propriétés complètes telles que la résistance, la ténacité et la plasticité de la résistance aux forces externes, et la couche résistante à l'usure en alliage fournit des propriétés résistantes à l'usure qui répondent aux exigences des conditions de travail spécifiées.
2. La couche et la plaque de base en alliage en alliage en alliage en acier sont en acier sont une combinaison métallurgique. Au moyen d'un équipement spécial et d'un processus de soudage automatique, le fil d'alliage auto-protectable de forte dureté est uniformément soudé sur le substrat, et les couches composites sont de une à deux ou encore plus. Dans le processus composite, en raison des différents rapports de retrait de l'alliage, des fissures transversales uniformes apparaissent, qui est une caractéristique significative de la plaque d'acier résistante à l'usure.
3.La couche résistante à l'usure de l'alliage est principalement en alliage de chrome, tandis que le manganèse, le molybdène, le niobium, le nickel et d'autres alliages sont ajoutés. La microdureté du carbure peut atteindre HV1700-2000, et la dureté de surface peut atteindre HRC58-62. L'alliage de carbure a une forte stabilité à haute température, maintiendra une dureté élevée, mais a également une bonne résistance à l'oxydation, dans les 500 ℃ Utilisation complètement normale.
4.La couche résistante à l'usure a un canal étroit (2,5 à 3,5 mm), un canal large (8-12 mm), une courbe (S, W), etc. Il est principalement composé d'alliage de chrome, tandis que le manganèse, le molybdène, le niobium, le nickelon , le bore et d'autres composants en alliage sont ajoutés. Avec une teneur en carbure de 40 à 60%, la microdureté peut atteindre HV1700 et la dureté de surface peut atteindre HRC58-62.
Product |
Wear Resistant Steel Plate |
Standard |
AISI,ASTM,DIN,JIS,GB,JIS,SUS,EN,etc. |
Thickness |
3-120mm |
Width |
600-1500mm, 1800-2000mm,2500-3500mm |
Length |
2000-3000mm, 6000-12000mm |
Grade |
NM360, NM400, NM450, NM500, AR360, AR400, AR450, AR500, AR550
QUARD400, QUARD450, QUARD500, FORA400, FORA500, RAEX400, RAEX450, RAEX500 |
Surface treatment |
Clean, blasting and painting according to customer requirement |
Technique |
Cold rolled and hot rolled |
Capacity |
10000 tons/month |
Package |
Export standard packing: wooden cases or boxes to be packed;We will pack the goods according to the factory's requirements for export. Or according to customer requirements.In addition,we will give the product good surface protection. |
Application |
metallurgy, coal, cement, power stntion, mining, building materials, petrochemical industry |
NM360 NM 400 NM 450 NM 500 Plaque d'acier de résistance à l'usure
Composant chimique
Steel/Grade |
C |
Si |
Mn |
P |
S |
AL |
Cr+Ni+Mo |
Nb+V+Ti |
NM360/AR360 |
0.10-0.30 |
0.20-0.40 |
1.00-2.00 |
≤0.015 |
≤0.003 |
≥0.20 |
<0.6 |
Trace Amount |
NM400/AR400 |
0.10-0.40 |
0.20-0.40 |
1.00-2.00 |
≤0.015 |
≤0.003 |
≥0.20 |
<0.9 |
|
NM450/AR450 |
0.10-0.40 |
0.20-0.40 |
1.00-2.00 |
≤0.015 |
≤0.003 |
≥0.20 |
<1.2 |
|
NM500/AR500 |
0.10-0.40 |
0.20-0.45 |
1.00-2.00 |
≤0.015 |
≤0.003 |
≥0.20 |
<1.5 |
|
NM550/AR550 |
0.10-0.50 |
0.20-0.45 |
1.00-1.50 |
≤0.015 |
≤0.003 |
≥0.20 |
<2.0 |
|
NM600/AR600 |
0.10-0.50 |
0.20-0.45 |
1.00-1.50 |
≤0.015 |
≤0.003 |
≥0.20 |
<2.5 |
Propriétés mécaniques
Material |
Tensile MPA |
Elongation% |
Impact energy -20℃ |
HBW |
NM300 |
≥1000 |
≥14 |
≥24 |
270-300 |
NM360 |
≥1100 |
≥12 |
≥24 |
330-390 |
NM400 |
≥1200 |
≥10 |
≥24 |
370-430 |
NM450 |
≥1250 |
≥7 |
≥24 |
420-480 |
NM500 |
≥1250 |
≥7 |
≥24 |
≥470 |
NM550 |
≥1250 |
≥7 |
≥24 |
≥530 |
NM600 |
≥1250 |
≥7 |
≥24 |
≥570 |
Nous pouvons produire différentes tailles, épaisseurs, largeurs et matériaux en fonction de vos exigences
1) Technique de fabrication
Couper les grandes plaques en acier comme exigences pour rendre la surface de la plaque brillante par le pilier et le broyage, peut également faire des trous et faire des degrés d'angle, et peut souder par votre dessin.
Pour l'épaisseur de moins de 30 mm, découpe par laser; Pour une épaisseur supérieure à 30 mm, principalement la coupe de la flamme.
Pour la plaque d'acier de 200 mm d'épaisseur, car pendant la coupe des flammes, la température est très élevée, de sorte que la plaque d'acier des pièces de coupe peut être cassée à la partie d'angle, puis nos travailleurs répareront les angles en bon état.
2 ) Application
Une plaque d'acier à usure avec une résistance à l'usure élevée et une bonne performance d'impact sont bonnes, peuvent être la coupe, la flexion, le soudage, etc., peut adopter le soudage, le soudage du bouchon, la façon de connexion des boulons pour se connecter avec d'autres structures, telles que la scène de l'entretien Le processus possède les caractéristiques de la déchets de temps, de pratique et largement utilisés dans la métallurgie, le charbon, le ciment, la centrale électrique, le verre, l'exploitation minière, les matériaux de construction, la brique et l'industrie pétrochimique, par rapport à d'autres matériaux, a une performance à coût élevé, a été favorisé par plus et plus d'acheteurs.
À propos de nous
Nous contacter
Copyright © 2024 SHANDONG HUITONG STEEL CO.,LTDTous droits réservés.
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.